Reinforced Flame Retardant PP+POE Granules(V0, Halogen-free)

Description
PP is the base resin and it is uniformly mixed with fire retardant, glass fiber, POE and processing modifier in a high speed. After twin-screw kneading granulation, reinforced polypropylene compound (PP+POE granules) is formed. Its flame retardant grade is UL94 V-0. This halogen free flame retardant compound owns excellent mechanical strength, excellent resistance to stress cracking, heat resistance and good workability. This reinforced polypropylene compound is used for electroplating processing and also applied in home appliances, electronic appliances and other fields.

Specifications of Halogen Free Flame Retardant Compound (PP+POE Granules)

Properties ASTM Test Condition Unit Typical Values
Physical Properties
Density D-792 23℃ g/cm3 1.18
Melt Flow Index D-1238 230℃ / 2.16 kg g/10min 3-6
Mold Shrinkage D-955 23℃ % 0.8-1.2
Mechanical Properties of Reinforced Polypropylene Compound (PP+POE Granules)
Tensile Strength D-638 10 mm / min MPa 38
Elongation at Break D-638 10 mm / min % 15
Flexural Strength D-790 2 mm / min MPa 60
Flexural Modulus D-790 2 mm / min MPa 2000
IZOD Impact Strength Notched D-256 3.2 mm, 23℃ KJ/m2 12
Thermal Properties of Halogen Free Flame Retardant Compound (PP+POE Granules)
Heat Distortion Temperature D-648 0.45 MPa, 6.4 mm 110
Vicat Softening Temperature D1525 1 kg, 120℃/h 150
Others
Flammability UL-94 1.6 mm V0

Note: Typical values are the average data from laboratory. They are only for use reference and are not the standards for products.

Processing Conditions of Reinforced Polypropylene Compound (PP+POE Granules)

  Unit Range
Melt Temperature 160-200
Barrel Temperature Rear 160-180
Center 170-190
Front 180-195
Mold Temperature 50
Mold Pressure   Pre-dry Requirements 80-100℃, 2-4 h

Note: The above-mentioned data is just for injection molding machine. According to different models, molds and specific requirements of halogen free flame retardant compounds, we can make appropriate adjustments.

Shanghai Info New Material Technology Co., Ltd. is a China exporter and supplier that can provide reinforced polypropylene compounds (PP+POE granules) for sale. Oriented by customers’ demands, our company is also engaged in producing various high-performance and functional modified plastic particles, sheets and film products. With strong R & D strength, we focus on the development and application of polyolefin (PP/PE), nylon (PA) modified products and composite materials. We are able to provide high quality halogen free flame retardant compounds for customers. Our reinforced polypropylene compounds have been exported to mainland, Hong Kong, Macao and Taiwan regions, North America, South America, Western Europe, Eastern Europe, East Asia, Southeast Asia, Middle East, Africa, Oceania, etc.

  • Reinforced Flame Retardant PP+EPDM Granules(V0, Halogen Free)
  • Reinforced Flame Retardant PP+EPDM Granules (V0, Halogen Free)Adopting PP as the base resin and evenly mixing it with fire retardant, glass fiber, EPDM and processing modifier in a high speed. After twin-screw kneading granulation, reinforced flame retardant EPDM compound granules (PP+EPDM) are produced. Its flame retardant grade is UL94 V-0. This reinforced polypropylene compoundpossesses excellent mechanical strength, excellent resistance to stress cracking ...