Halogen Free Flame Retardant PE Granules（1.6 mm V0）

Description
PE is the base resin and it is evenly mixed with antioxidant, halogen-free flame retardant and processing modifier in a high speed, non-halogen flame retardant polyethylene granules come into being after twin-screw kneading granulation. Its flame retardant grade reaches UL94 V-0 (1.6 mm). It possesses the advantages of excellent resistance to stress cracking, low temperature resistance and impact resistance. Halogen free flame retardant PE granules are extensively used in home appliances, auto spare parts, wire and cable and other fields. With advanced technological equipment, tremendous technical strength and reliable product quality, our non-halogen flame retardant polyethylene granules have received a number of favorable comments from customers.

Parameters of Halogen Free Flame Retardant PE Granules（1.6 mm V0）

Properties	ASTM	Test Condition	Unit	Typical Values
Physical Properties
Density	D-792	23℃	g/cm3	1.15
Melt Flow Index	D-1238	230℃ / 2.16 kg	g/10min	0.5-5
Mold Shrinkage	D-955	23℃	%	1.2-1.6
Mechanical Properties of Non-Halogen Flame Retardant Polyethylene Granules
Tensile Strength	D-638	10 mm / min	MPa	18
Elongation at Break	D-638	10 mm / min	%	150
Flexural Strength	D-790	2 mm / min	MPa	25
Flexural Modulus	D-790	2 mm / min	MPa	420
IZOD Impact Strength Notched	D-256	3.2 mm, 23℃	KJ/m2	10
Thermal Properties
Heat Distortion Temperature	D-648	0.45 MPa, 6.4 mm	℃	50
Others
Flammability	UL-94	1.6 mm	—	V0

Note: Typical values are the average data from laboratory. They are only for use reference and are not the standards for products.

Processing Conditions of Non-Halogen Flame Retardant Polyethylene Granules

		Unit	Range
Melt Temperature		℃	110-150
Barrel Temperature	Rear	℃	110-140
	Center	℃	120-140
	Front	℃	130-150
Mold Temperature.		℃	40
Mold Pressure		Pre-dry Requirements	60-80℃, 2-4 h

Note: The above-mentioned data is just for injection molding machine. According to different models, molds and specific requirements of products, we can make appropriate adjustments.

Shanghai Info New Material Technology Co., Ltd. is a China high-tech enterprise engaged in research and development of modified plastics. In addition to non-halogen flame retardant polyethylene granules, we also offer other high-performance and functional modified plastic particles, sheets and film products for sale, such as PP+POE granules, PP granules, PP+EPDM granules, polyethylene hydroxide granules, PE + magnesium hydrate granules, PE + aluminum hydrate granules, etc. Our company is capable of designing, manufacturing, assembling and testing non-halogen flame retardant polyethylene granules. Our products are exported to mainland, Hong Kong, Macao and Taiwan regions, North America, South America, Western Europe, Eastern Europe, East Asia, Southeast Asia, Middle East, Africa, Oceania, etc.