Halogen Free Flame Retardant PP+EPDM Granules（1.6 mm V0）

Description
Choosing PP as the base resin and uniformly mixing it with halogen-free fire retardant, EPDM (Ethylene-Propylene-Diene Monomer) and processing modifier in a high speed, halogen free flame retardant EPDM compound granules are formed after twin-screw kneading granulation. Its flammability level is UL94 V-0 (1.6 mm). This halogen free flame retardant compound possesses excellent mechanical strength, excellent resistance to stress cracking, heat resistance and good workability. It is widely used for electroplating processing and applied in home appliances, electronic appliances and other fields. Our company is a professional supplier of flame retardant EPDM compound granules (PP+EPDM) in China. Our halogen free flame retardant compounds can also be used on cable sheath for subway, mine, ship and warship applications.

Applications
The halogen free flame retardant EPDM compound granules are extensively used for insulation sheets, power supplies, switching components, thermostats, relay housings, circuit breakers, low voltage electrical appliances shell, TV or monitors, business computers, etc.

Features
1. This halogen free flame retardant compound (PP+EPDM granule) features low water absorption and good overall performance.
2. TallKee non-halogen flame retardant EPDM compound granules can be used under high humidity environments.
3. Electrical accessories meet all stringent requirements.
4. Our halogen free flame retardant compounds (1.6 mm V0) have excellent machining property and good flame retardant property.
5. Non-halogen flame retardant EPDM compound granules have excellent heat resistance.

Process
This halogen free flame retardant compound (PP+ EPDM granule) can be extruded and molded by a general screw extruder. The extruding velocity and temperature can be adjusted appropriately according to specific requirements.

Packaging Specification
We use kraft bags with plastic bag lining to package flame retardant EPDM compound granules.

Details of Halogen Free Flame Retardant Compound (PP+ EPDM Granules)

Properties	ASTM	Test Condition	Unit	Typical Values
Physical Properties
Density	D-792	23℃	g/cm3	1.10
Melt Flow Index	D-1238	230℃ / 2.16 kg	g/10min	3-6
Mold Shrinkage	D-955	23℃	%	1.2-1.5
Mechanical Properties of Flame Retardant EPDM Compound Granules
Tensile Strength	D-638	10 mm / min	MPa	28
Elongation at Break	D-638	10 mm / min	%	200
Flexural Strength	D-790	2 mm / min	MPa	45
Flexural Modulus	D-790	2 mm / min	MPa	1100
IZOD Impact Strength Notched	D-256	3.2 mm, 23℃	KJ/m2	15
Thermal Properties of Halogen Free Flame Retardant Compound (PP+ EPDM Granules)
Heat Distortion Temperature	D-648	0.45 MPa, 6.4 mm	℃	100
Vicat Softening Temperature	D1525	1 kg, 120℃/h	℃	145
Others
Flammability	UL-94	1.6 mm	—	V0

Note: Typical values are the average data from laboratory. They are only for use reference and are not the standards for products.

Processing Conditions of Non-Halogen Flame Retardant EPDM Compound Granules

		Unit	Range
Melt Temperature		℃	160-200
Barrel Temperature	Rear	℃	160-180
	Center	℃	170-190
	Front	℃	180-195
Mold Temperature.		℃	50
Mold Pressure		Pre-dry Requirements	80-100℃; 2-4 h

Note: The above-mentioned data is just for injection molding machine. According to different models, molds and specific requirements of products, we can make appropriate adjustments.